PENGARUH PENGGUNAAN BUR HALUS PADA KEKASARAN PERMUKAAN OKLUSAL TERHADAP KEKUATAN TARIK SEMEN LUTING
Article Info   ABSTRACT
Published date:
23 Jan 2015
 
Abstract On one side surface preparation needs roughness, but on the other hand, smoothing also needs to be done. Up to now there has been no data about the effect of smoothing on the preparation walls using a carbide bur against the tensile strength of luting cement. Tensile stress which will release a fixed restoration of the place would cause strength of the luting cement called tensile strength. The study was conducted to know the effect of smoothing the occlusal preparation walls on the tensile strength of luting cement on metal plate. This was an experimental study with posttest-only control group design. Tooth specimens that have been prepared by three different burs (coarse diamond bur, fine diamond bur, and coarse diamond bur and fine carbide bur) cemented by the luting cement (glass ionomer or zinc phosphate) to the metal plate. The metal was pulled out by using tensile strength tester (AM 100 Galdabini). Data obtained was processed to determine the strength of its appeal, analyzed by one-way ANOVA test and followed by LSD test if obtained significant results. The results showed that the smooth preparation had greater tensile strength (0.47 N/mm2) than those which were not smooth (0.25 N/mm2). Statistical tests showed that there was an effect of smoothing preparation wall of the luting cement on the tensile strength of the metal plate (p<0.05). In conclusion, the smoothing of the preparation walls that can deliver the highest tensile strength of the luting cement was prepared with a coarse diamond bur and then polished with a fine carbide bur. Key words: smoothing, tensile strength, luting cementAbstrak Di satu sisi perlu kekasaran pada permukaan preparasi, akan tetapi di sisi lain penghalusan juga perlu dilakukan. Sampai saat ini, belum ada data mengenai pengaruh penghalusan dinding preparasi menggunakan bur karbit terhadap kekuatan tarik semen luting. Tekanan tarik yang akan melepaskan suatu restorasi cekat dari tempatnya akan menimbulkan tahanan dari semen luting yang disebut kekuatan tarik. Penelitian ini dilakukan untuk mengetahui pengaruh penghalusan permukaan oklusal preparasi terhadap kekuatan tarik semen luting pada lempeng logam. Penelitian ini menggunakan rancangan eksperimen posttest-only control group design. Spesimen gigi yang telah diasah dengan 3 bur yang berbeda (bur intan coarse, bur intan fine, dan bur intan coarse + bur karbit fine) diberi semen luting (ionomer kaca atau zinc phosphate) untuk menyemen lempeng logam. Logam ditarik dengan alat uji kekuatan tarik (PM 100 Galdabini). Data yang diperoleh diolah untuk menentukan kekuatan tariknya, dianalisis dengan uji Anova satu arah dan dilanjutkan dengan uji LSD jika diperoleh hasil yang signifikan. Hasil penelitian menunjukkan bahwa penghalusan hasil preparasi mempunyai kekuatan tarik lebih besar (0,47 N/mm2) dibandingkan yang sama sekali tidak dihaluskan (0,25 N/mm2). Uji statistik menunjukkan ada pengaruh penghalusan dinding preparasi terhadap kekuatan tarik semen luting pada lempeng logam (p<0,05). Sebagai kesimpulan, penghalusan dinding preparasi yang dapat memberikan kekuatan tarik yang paling tinggi bagi semen luting adalah yang dipreparasi dengan bur intan coarse dan kemudian dihaluskan dengan bur karbit fine. Kata kunci: penghalusan, kekuatan tarik, semen luting