Journal > Seminar Nasional Teknik Kimia Kejuangan > Fotoreduksi Logam Krom (VI) Menggunakan Fotokatalis Lapis Tipis TiO2-Mn Mesopori dengan Bantuan Lampu Tungsten

 

Full Text PDF (310 kb)
Seminar Nasional Teknik Kimia Kejuangan
2016: Prosiding SNTKK 2016
Fotoreduksi Logam Krom (VI) Menggunakan Fotokatalis Lapis Tipis TiO2-Mn Mesopori dengan Bantuan Lampu Tungsten
Riyani, Kapti ( Jurusan Kimia FMIPA Universitas Jenderal Soedirman)
Setyaningtyas, Tien ( Jurusan Kimia FMIPA Universitas Jenderal Soedirman)
Soleh, Agus ( Jurusan Kimia FMIPA Universitas Jenderal Soedirman)
Article Info   ABSTRACT
Published date:
20 Apr 2016
 
Hexavalent chromium is a heavy metal that is toxic and give bad impact to human living. Maximum consentration of hexavalent chromium of solution that can be accepted is 0,05 ppm. This research was conducted to reduce hexavalent chromium by photoreduction method using mesophorous TiO2-Mn thin film photocatalyst with a tungsten lamp. Tha aim of this research is to obtain optimum ratio of TiO2-Mn (100:0; 99:1; 98:2; 97:3; and 96:4) to reduce hexavalent chromium. A thin film was synthesized by photodeposition method with calcination temperature 4000C for 6 hours. TiO2-Mn was crushed and made into coloidal phase with PEG 1000, then coated on a glass plat (9X4 cm). Thin film was tested to reduce hexavalent chromium with tungsten lamp and its concentration was measured by UV-Visible Spectrophotometer at wave length of 541 nm. The result showed that 99:1 is an optimum ratio of TiO2-Mn and it reduce hexavalent chromium up to 52,3 %. The decrease of hexavalent chromium concentration caused by the photoreduction process in mesophorous TiO2-Mn