Journal > YOUNGSTER PHYSICS JOURNAL > ANALISIS MIKROSTRUKTUR NANOPARTIKEL CeO2 DIDOPING Zn YANG DISINTESIS MENGGUNAKAN METODE PRESIPITASI

 

Full Text PDF (305 kb)
YOUNGSTER PHYSICS JOURNAL
Vol 2, No 2 (2013): Youngster Physics Journal April 2013
ANALISIS MIKROSTRUKTUR NANOPARTIKEL CeO2 DIDOPING Zn YANG DISINTESIS MENGGUNAKAN METODE PRESIPITASI
Futikhaningtyas, Ririn ( Jurusan Fisika Fakultas Sains dan Matematika Universitas Diponegoro)
Wahyu Puspaningrum, Nurul ( Jurusan Fisika Fakultas Sains dan Matematika Universitas Diponegoro)
Nurhasanah, Iis ( Jurusan Fisika Fakultas Sains dan Matematika Universitas Diponegoro)
Article Info   ABSTRACT
Published date:
23 Apr 2013
 
Zn-doped CeO2 nanoparticles with various Zn content of 0 - 20% have been synthesized by using precipitation method in the solvent mixture of aquades and isopropanol at room temperature.  The precipitant was calcinated at temperatur 300oC for 3 hours.  The structural properties of CeO2 nanoparticles were characterized by using x-ray diffraction.  X-ray diffraction pattern was analyzed to investigate the influence of Zn doping on crystalite size, lattice constant and lattice strain of CeO2 nanoparticle.  Observation to the peaks diffraction indicate that all of the CeO2 nanoparticle with various Zn doping have cubic fluorite structure and lattice constants in the range 5,4155 Å – 5,4254 Å.  The crystallite sizes of 6 – 11 nm were obtained by Williamson-Hall plot method.  Incorporation of Zn to the CeO2 nanoparticle decrease the crystallite size.  The crystallite size of Zn-doped CeO2 nanoparticles is depend on Zn%. Keywords: CeO2, nanoparticle, precipitation, lattice constant, x-ray diffraction